- HOME
- POLYMER SEARCH
- Thermoplastic
- ABS Polymer
- Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
- Diamond Polymers ABS TX-541
Diamond Polymers ABS TX-541
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS TX-541.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Super High Heat ABSInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
2.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
Procedure A; ASTM D1238 |
| 11.8 g/10 min @Load 5.00 kg, Temperature 265 °C |
11.8 g/10 min @Load 11.0 lb, Temperature 509 °F |
Procedure A; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 112 | 112 | ASTM D785 |
| Tensile Strength, Yield | 36.67 MPa | 5319 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.52 GPa | 366 ksi | Procedure B, Test Method I(chs 0.05 in/min); ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.90 ft-lb/in | Test Method A (0.125 in bar); ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 115 °C | 239 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 145 °C | 293 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 7.58 MPa | 700 - 1100 psi |
Users viewing this material also viewed the following:
- M. Holland Company PP204 Polypropylene Homopolymer
- Ineos Styrenics Avantra® 594E High Impact Styrenic Polymer (NAFTA)
- Karina 806-10/236-H-ISE White PVC Compound
- Schott N-SF57 Glass
- Silberline SilBerCote® 5245-20Z
- Zylog Neoplast® 173 FT EB Thermoplastic Vulcanizate
- Unipetrol Grade D Diesel Oil
- A. Schulman FORMION™ FI 105 Non-Reinforced, Injection Molding Grade Sodium Ionomer
- Hexcel® HexPly® F155 Epoxy Resin, 1581 Glass Fabric
- AK Steel TRAN-COR® H-1 CARLITE® Grain Oriented Electrical Steel
Copyright © lookpolymers.com All Rights Reserved