Diamond Polymers ABS 7600B (ELG)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS 7600B (ELG).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Blow Molding Grade, Extra High Impact, Low GlossInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 0.80 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.80 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Tensile Strength, Yield | 40.7 MPa | 5900 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 1.90 GPa | 275 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 4.27 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
8.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | 0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648 |
| 96.1 °C | 205 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 104 °C | 220 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 6.0 % | 6.0 % | Specular Gloss, Texture MT, 11030 Geometry 60°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Higher mold temperature provides a product with excellent surface finishing and less residual stress. |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Injection Pressure | 4.83 - 6.21 MPa | 700 - 900 psi |
Users viewing this material also viewed the following:
- Renegade Materials Corporation RM-3002 Bismaleimide (BMI) Resin IM7 12K Carbon Uni-tape
- MV Labs W855 (NH4)6H2W12O40.xH2O Ammonium tungstate, meta
- Daelim H&L Plavis G40 Aromatic Polyimide, 40% Graphite Filled, Direct Formed (Unverified Data**)
- Huntsman Araldite 94-105 Water-Based Hardener
- Techmer ES HiFill® PA6 GF15 UV002 15% Glass Filled
- Shin-Etsu Silicones KE-3421 Silicone, RTV Conformal Coating
- Clariant Renol PPOSP0001 Polyphenylene Oxide, Mineral Filled
- 3M Scotch® 356 Transparent Label Protection Tape
- Barlog Plastics KEBAFLEX P D40.3 Polyester-Elastomer, Shore D40
Copyright © lookpolymers.com All Rights Reserved