Diamond Polymers ABS 3502ELG

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers ABS 3502ELG.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Injection Molding Grade, Medium Impact, Low GlossInformation provided by Diamond Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.06 g/cc
1.06 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 2.3 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 2.3 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 Procedure A Condition G; ASTM D1238
8.6 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 8.6 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 Procedure A Condition I; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 104
104
ASTM D785
Tensile Strength, Yield 40.0 MPa
5800 psi
chs 2 in/min; ASTM D638
Flexural Modulus 2.28 GPa
330 ksi
Tangent, chs 0.05 in/min; ASTM D790
Izod Impact, Notched 2.14 J/cm

@Thickness 3.17 mm,
Temperature 23.0 °C
 4.00 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
 bar; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 79.4 °C
175 °F
0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648
96.1 °C
205 °F
0.125 in bar Annealed 4 hours at 80°C; ASTM D648
Vicat Softening Point 103 °C
218 °F
0.125 inch, 1 Kg; ASTM D1525
UL RTI, Electrical 80.0 °C

@Thickness 1.50 mm
 176 °F

@Thickness 0.0591 in
 UL 746B
UL RTI, Mechanical with Impact 80.0 °C

@Thickness 1.50 mm
 176 °F

@Thickness 0.0591 in
 UL 746B
UL RTI, Mechanical without Impact 80.0 °C

@Thickness 1.50 mm
 176 °F

@Thickness 0.0591 in
 UL 746B
Flammability, UL94 HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Middle Barrel Temperature 200 - 220 °C
392 - 428 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Higher mold temperature provides a product with excellent surface finishing and less residual stress.
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 4.83 - 6.21 MPa
700 - 900 psi