- Beijing Chemical Industry KAIFA® M105N MPPO Resin
Beijing Chemical Industry KAIFA® M105N MPPO Resin
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® M105N MPPO Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flame retardant, Thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
38.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.7 @Frequency 1e+6 Hz |
2.7 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 °C | 500 °F | |
| Middle Barrel Temperature | 280 °C | 536 °F | |
| Front Barrel Temperature | 280 °C | 536 °F | |
| Nozzle Temperature | 275 °C | 527 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Injection Pressure | 120 MPa | 17400 psi | |
| Cycle Time - Injection | 35 sec | 35 sec | |
| Screw Speed | 70 rpm | 70 rpm |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S50H Silicone Rubber
- PolyOne Maxxam® RP81065 HIPS (discontinued **)
- Borealis Borcell™ LE1120 Low Density Polyethylene for Physically Foamed Cellular Insulation
- Unitika A1030TF PA6, Conditioned
- Cossa Polimeri ESTAPROP H 0560 GFCTG Polypropylene, 30% Mixed Filler
- ExxonMobil HDPE HD P8660.29 High Density Polyethylene Resin
- ExxonMobil Label-Lyte™ 612LLG102 OPP Film
- ExxonMobil Oppalyte™ 38ICE OPP Film
- Alliance Polymers Viprene™ G55A-32U-NAT Thermoplastic Vulcanizate Elastomer
- Bhansali Engineering Abstron KU603 ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved