DSM Novamid® ST145 NAT PA6-I
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® ST145 NAT PA6-I.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact Modified, Injection Molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.90 % | 1.90 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.022 cm/cm | 0.022 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | cond; ISO 527-1/-2 |
| 30.0 MPa | 4350 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | >= 50 % | >= 50 % | cond; ISO 527-1/-2 |
| >= 50 % | >= 50 % | dry; ISO 527-1/-2 | |
| Elongation at Yield | 8.8 % | 8.8 % | dry; ISO 527-1/-2 |
| 41 % | 41 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 0.360 GPa | 52.2 ksi | cond; ISO 527-1/-2 |
| 1.00 GPa | 145 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 16.0 MPa | 2320 psi | cond; ISO 178 |
| 39.0 MPa | 5660 psi | dry; ISO 178 | |
| Flexural Modulus | 0.380 GPa | 55.1 ksi | cond; ISO 178 |
| 1.10 GPa | 160 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
dry; ISO 179/1eU | |
| Charpy Impact, Notched | 10.9 J/cm² @Temperature 23.0 °C |
51.9 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C | 55.6 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | dry; ISO 11359-1/-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.0 °C | 144 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | dry; ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+14 ohm-cm | 9.00e+14 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 2.00e+13 ohm | 2.00e+13 ohm | cond; IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 100 Hz |
3.0 @Frequency 100 Hz |
dry; IEC 60250 |
| 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.010 @Frequency 100 Hz |
0.010 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- MV Labs LA500 LaF3 Lanthanum fluoride
- NanoAmor 95%, OD/ID/L: 8-15/3-5 nm/0.5-2 um Short Multi-Walled Carbon Nanotubes
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Hi-Sil 233 Filler
- Huntsman IROGRAN® A 85 P 4394 TPU-Polyether
- Lubriplate SPO-233 Petroleum-Based Gear, Bearing, & Recirculating Oil
- LG Chemical Lupox® HI2303 PBT+GF30%
- SABIC Innovative Plastics Valox® 735 PBT (Asia Pacific)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 70 PHR N330 (HAF) Filler
- Chase Plastics CP Pryme® AC100-27 Acetal Copolymer Molding Resin
- Covestro Bayblend® T65 AT PC/ABS Blend
Copyright © lookpolymers.com All Rights Reserved