DSM Novamid® 1015G33-8 NAT PA6-GF33
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | DSM Engineering Plastics |
| Trade Name | Novamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DSM Novamid® 1015G33-8 NAT PA6-GF33.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
33% Glass Reinforced, Injection Molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 2.30 % | 2.30 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 118 MPa | 17100 psi | cond; ISO 527-1/-2 |
| 185 MPa | 26800 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.0 % | 3.0 % | dry; ISO 527-1/-2 |
| 6.0 % | 6.0 % | cond; ISO 527-1/-2 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | cond; ISO 527-1/-2 |
| 9.80 GPa | 1420 ksi | dry; ISO 527-1/-2 | |
| Flexural Strength | 175 MPa | 25400 psi | cond; ISO 178 |
| 280 MPa | 40600 psi | dry; ISO 178 | |
| Flexural Modulus | 5.80 GPa | 841 ksi | cond; ISO 178 |
| 9.40 GPa | 1360 ksi | dry; ISO 178 | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eU |
| 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eU | |
| Charpy Impact, Notched | 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 2.20 J/cm² @Temperature 23.0 °C |
10.5 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C | 33.3 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | dry; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
dry; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 |
| Surface Resistance | 2.00e+14 ohm | 2.00e+14 ohm | cond; IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 100 Hz |
4.0 @Frequency 100 Hz |
dry; IEC 60250 |
| 4.0 @Frequency 1.00e+6 Hz |
4.0 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | dry; IEC 60243-1 |
| Dissipation Factor | 0.011 @Frequency 100 Hz |
0.011 @Frequency 100 Hz |
dry; IEC 60250 |
| 0.020 @Frequency 1.00e+6 Hz |
0.020 @Frequency 1.00e+6 Hz |
dry; IEC 60250 | |
| Comparative Tracking Index | 525 V | 525 V | dry; IEC 60112 |
Users viewing this material also viewed the following:
- Polymer Resources PPX-FR1-[color]-EN Modified-PPO, V-0 Flame Retardant, Extrusion Grade
- PolyMirae Moplen HP562S Fiber (Spunbond) Grade Polypropylene
- PolyOne Geon™ CPVC MC550 Polyvinyl Chloride, Chlorinated (CPVC)
- Haynes 188 alloy, hot rolled and 1175°C solution annealed plate
- Saint-Gobain Meldin® 2211 Bearing
- ExxonMobil LD 302.34 High Clarity, High Impact Film Resin
- Dow DNDA-8335 NT 7 Linear Low Density Polyethylene Resin
- Fainplast Compounds GS 64/BT Flexible PVC, Injection Molding for Footwear
- Atom Adhesives AA-DUCT 2924 Epoxy Adhesive
- Beijing Evergrow Resources Rayon Activated Carbon
Copyright © lookpolymers.com All Rights Reserved