Covestro Bayblend® FR 3008 HR Polycarbonate + ABS, Flame Retardant Grade

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Covestro
Trade Name Bayblend®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Covestro Bayblend® FR 3008 HR Polycarbonate + ABS, Flame Retardant Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Injection molding gradeHDT/A = 85 °CVicat/B 120 temperature = 103 °CUL-listing 94 V-0 (1.5 mm)improved chemical and very good hydrolysis resistance antimony-, chlorine- and bromine-free flame retardantglow wire test (GWFI): 960 °C (2.0 mm)no juicinggood light stabilityPreprocessingMax. Water content
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Water Absorption 0.50 %
0.50 %
Similar to ISO 62
Moisture Absorption at Equilibrium 0.20 %
0.20 %
Similar to ISO 62
Melt Flow 15 g/10 min

@Load 5.00 kg,
Temperature 240 °C
15 g/10 min

@Load 11.0 lb,
Temperature 464 °F
estimated from MVR using room temperature density; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 60.0 MPa
8700 psi
ISO 527-1/-2
Elongation at Yield 4.0 %
4.0 %
ISO 527-1/-2
Tensile Modulus 2.80 GPa
406 ksi
ISO 527-1/-2
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 76.0 µm/m-°C
42.2 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C
44.4 µin/in-°F
ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C
203 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
ISO 75-1/-2
Vicat Softening Point 101 °C
214 °F
50°C/h 50N; ISO 306
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
IEC 60695-11-10
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
IEC 60695-11-20
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.1

@Frequency 1.00e+6 Hz
3.1

@Frequency 1.00e+6 Hz
IEC 60250
3.2

@Frequency 100 Hz
3.2

@Frequency 100 Hz
IEC 60250
Dielectric Strength 30.0 kV/mm
762 kV/in
IEC 60243-1
Dissipation Factor 0.0050

@Frequency 100 Hz
0.0050

@Frequency 100 Hz
IEC 60250
0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 300 V
300 V
IEC 60112
Processing Properties Metric English Comments
Melt Temperature 240 °C
464 °F
Injection Molding; ISO 294
240 - 270 °C
464 - 518 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
80.0 °C
176 °F
Injection Molding; ISO 10724
Injection Velocity 240 mm/sec
9.45 in/sec
ISO 294
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
India
Near East/Africa
North America
South and Central America
Feature Release agent
Form Pellets
Process Injection Molding