Clariant Renol R60G33HSL Nylon 6, 33% Glass Fiber, Heat Stabilized, Lubricated, Economy
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol R60G33HSL Nylon 6, 33% Glass Fiber, Heat Stabilized, Lubricated, Economy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 221 MPa | 32000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm @Temperature 22.8 °C |
1.90 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 249 - 277 °C | 480 - 530 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture level is less than 0.02% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CM6140 PC+ABS
- DuPont Performance Polymers Hypalon® HPG-6525 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound &n
- Karina E 18/10-GIN Gray Aluminum MB (SP31454) for PVC
- Solvay Specialty Polymers Polymist® XPP 527 Polytetrafluoroethylene (PTFE)
- Shin-Etsu Silicones FEA-261U Fluorosilicone Elastomer
- ExxonMobil LL 1001x76 Blown Film Resin
- DuPont Performance Polymers Zytel® HTN 54G35EF BKB336 Polyphthalamide (PPA) (Unverified Data**)
- DuPont™ Bynel® 41E766 Anhydride Modified LLDPE
- Bulk Molding Compounds BMC T40(25)-XHS Die Casting Replacement Grade Molding Compound
- PolyOne Edgetek® SF-10GF/000 Polyphenylene Sulfide (PPS), Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved