Clariant Renol PPT20BN-346 Polypropylene Copolymer, Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PPT20BN-346 Polypropylene Copolymer, Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | ASTM D638 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 76.7 °C | 170 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 25.0 °C | 77.0 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 221 °C | 380 - 430 °F | |
| Mold Temperature | 51.7 - 65.6 °C | 125 - 150 °F | |
| Dry Time | 2 - 4 hour @Temperature 71.1 °C |
2 - 4 hour @Temperature 160 °F |
to avoid surface defects |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 925 PC (Asia Pacific)
- Fainplast Compounds RH 225 Rigid PVC, Antishock Extrusion
- Hyosung Topilene HJ740 PP
- Haynes Hastelloy® B-3® alloy, 10% cold work
- Plenco 00757 Melamine-Phenolic, Granular, Transfer Molded
- ChevronTexaco Havoline® SAE 85W-140 Gear Oil
- EMS-Grivory Grivory® LV-3 X ESD black PA12-GF30
- 3M GM110 Gripping Material
- Alliance BIS-56 Bonded (Composite) Magnetic Material
- Henkel Turco Liquid Sprayeze NP-LT Deoxidizer
Copyright © lookpolymers.com All Rights Reserved