- Polypropylene with 10% Talc Filler
- Clariant Renol PPT10 Polypropylene Copolymer, Talc Filled
Clariant Renol PPT10 Polypropylene Copolymer, Talc Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PPT10 Polypropylene Copolymer, Talc Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.980 g/cc | 0.980 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | ASTM D638 |
| Flexural Modulus | 1.65 GPa | 240 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 221 °C | 380 - 430 °F | |
| Mold Temperature | 51.7 - 65.6 °C | 125 - 150 °F | |
| Dry Time | 2 - 4 hour @Temperature 71.1 °C |
2 - 4 hour @Temperature 160 °F |
to avoid surface defects |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.000 - 1.72 MPa | 0.000 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Pasargad Polymer Peyvand Pasadur 3P-H8130B PBT, 30% Glass Fiber Reinforced
- Pinnacle Polymers 3220 Impact Polypropylene Copolymer, Injection Molding Grade
- Dow Pellethane® 2102-90AE Polyurethane Elastomer, Polyester Polycaprolactone Based (discontinued **)
- FloMet Fe-50% Ni Soft Magnetic Alloy
- Ineos ABS Lustran® 451 ABS, Injection Molding Grade
- Ferro EG 2992 Glaze and Sealant Glass
- Bhansali Engineering Abstron SE32H Extrusion ABS
- Akro-Plastic Akromid® B3 GF 15 S3 PA, Dry-Impact Resistant, 15% Glass Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved