Radici Heraform® R 900 Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Radici Group Plastics |
| Trade Name | Heraform® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Radici Heraform® R 900 Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard grade for injection molding of details with high mechanical requirement.Information provided by Radici group.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ISO 1183 |
| Water Absorption | 0.65 % | 0.65 % | ISO 62 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | ISO 527 |
| Elongation at Break | 30 % | 30 % | ISO 527 |
| Tensile Modulus | 2.85 GPa | 413 ksi | ISO 527 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ISO 178 |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 166 °C | 331 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 219 °F | ISO 75 |
| Vicat Softening Point | 150 °C @Load 5.10 kg |
302 °F @Load 11.2 lb |
ISO 306 |
| Flammability, UL94 | HB @Thickness 1.00 mm |
HB @Thickness 0.0394 in |
|
| Shrinkage | 1.8 % @Pressure 100 MPa, Temperature 90.0 °C |
1.8 % @Pressure 14500 psi, Temperature 194 °F |
3 mm |
Users viewing this material also viewed the following:
- PlastiComp Complet® LCF30 - TPU Rigid Thermoplastic Polyurethane, 30% Long Carbon Fiber Reinforced
- ND Industries 420 Instant High Pressure Pipe Sealant
- SABIC Innovative Plastics Lexan® 953 PC (Asia Pacific)
- Shamrock Technologies Fluoro T® 807 Thermoplastic Grade PTFE Additive
- Saint-Gobain CHR® SG36-10(R) Industrial Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Total HDPE 53090 High Density Polyethylene - Blow Molding
- DSM Arnitel® EM550 Polyether Ester Elastomer (European and Asian Grade)
- BNZ Materials BNZP-26A Insulating Firebrick (French Grade)
- Arlon 56609R028 0.029" Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Alliance BIN-55 Bonded (Composite) Magnetic Material
Copyright © lookpolymers.com All Rights Reserved