- Clariant Renol PBT1100TF10 Polybutylene Terephthalate, PTFE Lubricated
Clariant Renol PBT1100TF10 Polybutylene Terephthalate, PTFE Lubricated
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), PTFE Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PBT1100TF10 Polybutylene Terephthalate, PTFE Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | ASTM D638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D638 |
| Flexural Yield Strength | 86.2 MPa | 12500 psi | ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Temperature 22.8 °C |
0.700 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 232 - 254 °C | 450 - 490 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 121 °C |
2 - 4 hour @Temperature 250 °F |
to ensure moisture content is less than 0.05% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPH4404 PPC+PC
- Kinlead HSD11 Normal Grade Heat Sealable Film (thickness: 20 µm)
- Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes
- Crucible Steel CSM® 420 XL Stainless Steel
- Dow Primacor® 4608 Ethylene Acrylic Acid (EAA)
- Aclo Accutech Polypropylene Homopolymer HP0334G10M20CL Glass/Mineral Reinforced Coupled
- ArcelorMittal IF 300 High strength IF steel, Cold rolled
- Aaron Industries AAROPRENE® TFPP 2030 Talc Filled Polypropylene
- Huntsman PE2040 Injection Molding Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved