- Clariant Renol PA1SP0019 Nylon 66/PPS Alloy, 20% Glass, 20% Mineral
Clariant Renol PA1SP0019 Nylon 66/PPS Alloy, 20% Glass, 20% Mineral
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PA1SP0019 Nylon 66/PPS Alloy, 20% Glass, 20% Mineral.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 138 MPa | 20000 psi | ASTM D638 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 - 0.801 J/cm @Temperature 22.8 °C |
1.00 - 1.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 260 - 263 °C | 500 - 505 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 - 257 °C | 490 - 495 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 293 - 316 °C | 560 - 600 °F | |
| Mold Temperature | 93.3 - 121 °C | 200 - 250 °F | |
| Dry Time | <= 4 hour @Temperature 93.3 °C |
<= 4 hour @Temperature 200 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.552 - 0.862 MPa | 80.0 - 125 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 60 - 100 rpm | 60 - 100 rpm |
Users viewing this material also viewed the following:
- Fainplast Compounds RH 207/OP Rigid PVC, Antishock Extrusion
- Hong Kun Group 3,5-Dinitrotrifluorotoluene Pharmaceutical Intermediate
- Global PP-2540-K Polypropylene Block Copolymer
- Johnson Matthey SW 950 Platinum w/ 5% Iridium Jewelry Alloy
- Techmer ES HiFill® PA6 X BN071 EL MB Nylon 6
- A. Schulman POLYFORT™ FPP 1876 22% Mineral Filled Copolymer, UV Inhibited Polypropylene
- Carmel Olefins IPETHENE® 113 Low Density Polyethylene
- Arkema Group LOTADER® 3410 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
- Pyrotek ISOCAST Insulating Refractory Castable
Copyright © lookpolymers.com All Rights Reserved