Clariant Renol PA1SP0004 Nylon 66, High Impact Modified, ESD
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PA1SP0004 Nylon 66, High Impact Modified, ESD.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.4 MPa | 6000 psi | ASTM D638 |
| Flexural Yield Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 1.52 GPa | 220 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm @Temperature 22.8 °C |
15.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistivity per Square | 1.00e+11 ohm | 1.00e+11 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 238 - 266 °C | 460 - 510 °F | |
| Mold Temperature | 79.4 - 107 °C | 175 - 225 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.05% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- Ipiranga Petrochem GM 9450 F HDPE
- Sylvin Technologies 8960-80 Natural PVC Extrusion Compound
- Teknor Apex Monprene® MP-2850A Thermoplastic Elastomer
- Dow Corning SYL-OFF® SL 560 COATING
- Diamond Polymers PC-1500F Clear, Natural Polycarbonate
- Eurostar Starflam UF0033 PPA, Glass Fiber Filled, Flame Retardant, Injection Molded
- ATI Allegheny Ludlum Stainless Steel Type 201, 5% Cold Work (UNS S20100)
- BASF Ultramid® TG3S 15% Glass Filled PA6 (Conditioned)
- DuPont Bynel® 50E631 Adhesive Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved