- Solvay TECHNYL® A 218 V25 NAT BA PA66, 25% glass fiber, DRY
Solvay TECHNYL® A 218 V25 NAT BA PA66, 25% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 V25 NAT BA PA66, 25% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 25% of glass fiber, specially stabilized to improve its resistance to oils and greases, for injection molding.Available in: Asia PacificProduct Applications: TECHNYL® A 218 V25 NAT BA is recommended for molding parts exposed to high temperatures and in contact with oils and greases. Bearing housings are a typical example for which this formulation is suitable. This product is approved by major bearing manufacturers. This product is available in natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183/A |
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec |
0.90 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0085 cm/cm | 0.0085 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 170 MPa | 24700 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Flexural Strength | 260 MPa | 37700 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 85.0 kJ/m² | 40.4 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
15.0 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 262 °C | 504 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.800 - 3.20 mm |
HB @Thickness 0.0315 - 0.126 in |
1210 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO D 6006 Grey
- PolyOne Geon™ Vinyl Rigid Extrusion 87549 Polyvinyl Chloride, Rigid (PVC, Rigid)
- MV Labs TM200 TmBr3 Thulium bromide
- Eastman Tenite 264-10 CAB Cellulose Acetate Butyrate (discontinued **)
- Teknor Apex ELEXAR® EL 8431 Thermoplastic Elastomer
- Universal Wire Works BNi-1A (AMS 4776) Nickel Base Brazing Filler Metal
- Aclo Accucomp ABS ABS892BL High Heat Grade
- BASF Ultramid® A3WG10 50% Glass Filled PA66 (Dry)
- Solvay RHODAFAC® RS-710 Surfactant
Copyright © lookpolymers.com All Rights Reserved