- Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
- Chi Mei Polylac® PA-758R ABS - Transparent
Chi Mei Polylac® PA-758R ABS - Transparent
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-758R ABS - Transparent.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Transparent, Chemical Resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Melt Flow | 27 g/10 min @Load 10.0 kg, Temperature 220 °C |
27 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 95.0 MPa | 13800 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 33.0 MPa | 4790 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 60 % | 60 % | 50 mm/min; ISO 527 |
| Flexural Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | 5.10 J/cm² | 24.3 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179 |
| Impact | 11.0 | 11.0 | Impact Flexural Test Notched (KJ/m²) |
| 57.0 | 57.0 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | unannealed; ISO 75 |
| 96.0 °C | 205 °F | annealed; ISO 75 | |
| Vicat Softening Point | 94.0 °C @Load 5.00 kg |
201 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 97.0 °C @Load 5.00 kg |
207 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 102 °C @Load 1.00 kg |
216 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 105 °C @Load 1.00 kg |
221 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3975H TPE, PP Overmold or Standalone use
- Saint-Gobain Tygon® Transflow S3™ M-34-R Raw Milk Dairy Tubing Formulation
- SMAC SMACFOAM® 1250S-06 Damping Material
- Solvay MACKAM® 35 UL Surfactant
- Polyram RamLloy PB917G6 Nylon 6/Polypropylene Alloy, 30% Glass Fiber Reinforced
- Braskem GF4960 HDPE Blow Molding Polyethylene Homopolymer
- SABIC Innovative Plastics LNP VERTON RX970079 PA 66 (Europe-Africa-Middle East)
- Huntsman PE2049 Injection Molding Polyethylene (discontinued **)
- Solvay RHODAPHOSE® TRIPHENYL PHOSPHINE Phosphorus Derivative
Copyright © lookpolymers.com All Rights Reserved