CRP Technology Windform® XT 2.0 Polyamide-Carbon Fiber Composite

Category Polymer , Rapid Prototyping Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer CRP Technology
Trade Name Windform®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF CRP Technology Windform® XT 2.0 Polyamide-Carbon Fiber Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Processed by selective laser sintering (SLS). Windform® XT 2.0 is the evolution of the ground breaking high performance Windform® XT, the carbon fiber reinforced composite material, known for its mechanical properties, which made it particularly suitable in demanding applications such as motorsport sector, aerospace and UAV’s. Windform® XT 2.0 is an innovative material, and replaces the Windform® XT, as the “Top Level” of the current Windform® range. Windform® XT 2.0 improves mechanical properties compared to “traditional” Windform® XT, while maintaining the same workability for Laser Sintering machines in order to better fulfill the needs of Additive Manufacturing required to produce end use parts and prototypes. Windform® XT 2.0 retains the matte black colour of the previous version and features improvements in mechanical properties: +8% in tensile strength, +22% in tensile modulus and +46% increase in elongation at break. Windform XT® 2.0allows for the creation of accurate, reliable and durable prototypes and is perfect for functional applications.Sample applications: Windform® XT 2.0 is the high-tech material for Additive Manufacturing chosen by those working in the Motorsport, Automotive (suitable for example for components under the hood, such as intake manifolds and functional cooling ducts), Air (for components UAV, Unmanned Aerial Vehicle) Aerospace (useful also to create prototype satellite, such as the CubeSat) and Design, as it allows applications that are fully functional, as well as bench testing, or testing and racing on the track.Information provided by CRP Technology.
Physical Properties Metric English Comments
Density 1.097 g/cc
0.03963 lb/in³
Mechanical Properties Metric English Comments
Tensile Strength at Break 83.84 MPa
12160 psi
UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97)
Elongation at Break 3.8 %
3.8 %
UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97)
Tensile Modulus 8.928 GPa
1295 ksi
UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97)
Flexural Strength 133.0 MPa
19290 psi
UNI EN ISO 14125: 2000
Flexural Modulus 7.338 GPa
1064 ksi
UNI EN ISO 14125: 2000
Izod Impact, Notched (ISO) 5.30 kJ/m²
2.52 ft-lb/in²
ISO 180:2000
Izod Impact, Unnotched (ISO) 19.26 kJ/m²
9.165 ft-lb/in²
ISO 180:2000
Charpy Impact Unnotched 2.243 J/cm²
10.67 ft-lb/in²
ISO 179-1:2007
Charpy Impact, Notched 0.472 J/cm²
2.25 ft-lb/in²
ISO 179-1:2007
Thermal Properties Metric English Comments
Melting Point 179.3 °C
354.7 °F
ISO 11357-2
Deflection Temperature at 1.8 MPa (264 psi) 173.4 °C
344.1 °F
ISO 75-2 TYPE A
Vicat Softening Point 176.1 °C
349.0 °F
10 N; ISO 306 TYPE A50
Electrical Properties Metric English Comments
Volume Resistivity <= 1e+8 ohm-cm
<= 1e+8 ohm-cm
ASTM D257-93
Surface Resistance <= 1e+8 ohm
<= 1e+8 ohm
ASTM D257-93
Descriptive Properties Value Comments
Color Black
Surface Finish 1.8 Ra µm
After Finishing
6.0 Ra µm
After SLS Process