- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Chi Mei Polylac® PA-747S ABS - Extrusion
Chi Mei Polylac® PA-747S ABS - Extrusion
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-747S ABS - Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High Impact Extrusion
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 4.4 g/10 min @Load 5.00 kg, Temperature 230 °C |
4.4 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 101 | 101 | ASTM D785 |
| Ball Indentation Hardness | 89.0 MPa | 12900 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ISO 527 |
| Flexural Strength | 57.0 MPa | 8270 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 3.93 J/cm @Thickness 3.17 mm |
7.36 ft-lb/in @Thickness 0.125 in |
|
| Izod Impact, Notched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 3.10 J/cm² | 14.8 ft-lb/in² | ISO 179 |
| Impact | 19.0 | 19.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | unannealed; ISO 75 |
| 96.0 °C | 205 °F | annealed; ISO 75 | |
| Vicat Softening Point | 98.0 °C @Load 5.00 kg |
208 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 102 °C @Load 5.00 kg |
216 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 103 °C @Load 1.00 kg |
217 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 106 °C @Load 1.00 kg |
223 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4912 TPE, Transparent
- Pacific Sintered Materials FS-1601 Silicon Iron Soft Magnetic Powdered Metal
- Iran Petrochemical (PCC) 5030UA High Density Polyethylene
- Solvay Specialty Polymers Ryton® R-4 Polyphenylene Sulfide (PPS), 40% Glass Fiber
- SMAC SMACWRAP® EX Damping Material, 0.12 mm
- Teknor Apex Telcar® TL-2590F Thermoplastic Elastomer
- Dow DOWLEX™ NG 3347A Linear Low Density Polyethylene, Ethylene-Octene Copolymer
- Dow Tyril® 990 SAN
- BASF Ultramid® B3WG6 CR BK 23210 15% Glass Filled (Dry)
- Lanxess Pocan® B 3225 Z 000000 PBT, 20% Glass Fiber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved