Aremco Ceramabond™ 503 High Temperature Ceramic Adhesive/Paste, Alumina Filled
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Aremco |
| Trade Name | Ceramabond™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aremco Ceramabond™ 503 High Temperature Ceramic Adhesive/Paste, Alumina Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aremco's ceramic adhesives are easy to use, one- and two-component systems which air dry in 1-2 hrs and are ready for use following a 200 to 700 °F cure. These materials are mostly water-based and do not outgas after curing. They are also environmentally safe, non-flammable materials which contain no volatile organic compounds.General Features: High Fired Strength Bonding: Ceramic to Ceramic Principal Use: Dense Ceramics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.35 - 2.55 g/cc | 0.0849 - 0.0921 lb/in³ | |
| Volatile Organic Compounds (VOC) Content | 0.000 g/l | 0.000 g/l | |
| Viscosity | 50000 - 90000 cP | 50000 - 90000 cP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Impact Test | 81.3 J | 60.0 ft-lb | Torque Strength; curing at 1000°F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.20 µm/m-°C | 4.00 µin/in-°F | |
| Maximum Service Temperature, Air | 1650 °C | 3000 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 6.73 kV/mm | 171 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 50.0 - 90.0 °C | 122 - 194 °F | Application |
| Cure Time | 120 min @Temperature 93.3 °C |
2.00 hour @Temperature 200 °F |
Step 1, preceeded by <1 hour air set |
| 120 min @Temperature 260 °C |
2.00 hour @Temperature 500 °F |
Step 2 | |
| 120 min @Temperature 371 °C |
2.00 hour @Temperature 700 °F |
Step 3 | |
| Shelf Life | 6.00 Month @Temperature 4.44 - 32.2 °C |
6.00 Month @Temperature 40.0 - 90.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Excellent | after curing at 700°F for 2 hours |
| Alkali Resistance | Fair | after curing at 700°F for 2 hours |
| Color | White | |
| Moisture Resistance | Good | after curing at 700°F for 2 hours |
| Solvent | Water | |
| Thinner | 503-T |
Users viewing this material also viewed the following:
- Kraton® G1657 + PA-6,6 blend (16/4/80)
- KB Alloys 36% Silicon Aluminum Alloy
- SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS
- Solvay Specialty Polymers Catalyst PS/2LR Polyolefin
- Techmer ES HiFill® PA6/6 GF50 L BK 50% Glass Filled (Dry)
- SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP
- Unipetrol PP MONSTEN® GB 005 Polypropylene Homopolymer
- BASF Novolen® 1100 L Polypropylene, Injection Molding Grade
- Arkema Group Pebax® MX 1205 SP 01 Polyether Block Amide (PEBA)
Copyright © lookpolymers.com All Rights Reserved