Arlon 28540R015 0.016" (0.406 mm) Uncured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 28540R015 0.016" (0.406 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Interleave: Polyethylene Side 1: Uncured Silicone RubberSubstrate: 1528 Style FiberglassAppearance: Red silicone gum on fiberglass clothThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	76.2 microns	3.00 mil	Interleave
	203 microns	8.00 mil	Side 1; Arlon SQA-TMS-003
	203 microns	8.00 mil	Substrate; Arlon SQA-TMS-003
	406 microns	16.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	47	47	Silicone Property; ASTM D2240
Tensile Strength	6.89 MPa	1000 psi	Silicone Property; ASTM D412
Elongation at Break	400 %	400 %	Silicone Property; ASTM D412
Peel Strength	1.74 kN/m	9.90 pli	Bond Strength; Arlon SQA-TMS-023

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-73.3 °C	-100 °F
Flammability Test	1.3	1.3	[in], Char; FTMS 191A, Method 5903
	6.0	6.0	[sec], Flame/Glow; FTMS 191A, Method 5903

Processing Properties	Metric	English	Comments
Cure Time	8.00 min @Pressure 0.552 MPa, Temperature 138 °C	0.133 hour @Pressure 80.0 psi, Temperature 280 °F	Bond Cycle
Shelf Life	6.00 Month @Temperature 23.9 °C	6.00 Month @Temperature 75.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Red
Total Product Weight (oz/yd2)	14.6	Arlon SQA-TMS-025