Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Plating Grade
Manufacturer Chi Mei Corporation (ChiMei)
Trade Name Polylac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chi Mei Polylac® PA-726 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Electro-plating
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Ball Indentation Hardness 99.0 MPa
14400 psi
H358/30; ISO 2039-1
Tensile Strength at Break 35.0 MPa
5080 psi
50 mm/min; ISO 527
Tensile Strength, Yield 44.0 MPa
6380 psi
50 mm/min; ISO 527
Elongation at Break 40 %
40 %
50 mm/min; ISO 527
Flexural Strength 64.0 MPa
9280 psi
2 mm/min; ISO 178
Flexural Modulus 2.10 GPa
305 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
ISO 180/1C
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 2.60 J/cm²
12.4 ft-lb/in²
ISO 179
Impact 18.0
18.0
Impact Flexural Test Notched (KJ/m²)
NB
NB
Impact Flexural Test Unnotched (KJ/m²)
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
unannealed; ISO 75
96.0 °C
205 °F
annealed; ISO 75
Vicat Softening Point 94.0 °C

@Load 5.00 kg
 201 °F

@Load 11.0 lb
 50°C/hr; ISO 306
96.0 °C

@Load 5.00 kg
 205 °F

@Load 11.0 lb
 120°C/hr; ISO 306
103 °C

@Load 1.00 kg
 217 °F

@Load 2.20 lb
 50°C/hr; ISO 306
103 °C

@Load 1.00 kg
 217 °F

@Load 2.20 lb
 120°C/hr; ISO 306
Flammability, UL94 HB

@Thickness 1.59 mm
 HB

@Thickness 0.0625 in
 UL 94