SABIC Innovative Plastics LNP Thermocomp QF008R PA 6/10

Category Polymer , Thermoplastic , Nylon , Nylon 610
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp QF008R PA 6/10.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* QF008R is a compound based on Nylon 6/10 containing Glass Fiber. Characteristics of this grade are: Easy Release.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ASTM D 792
1.42 g/cc
0.0513 lb/in³
ISO 1183
Mechanical Properties Metric English Comments
Tensile Strength at Break 171 MPa
24800 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 3.3 %
3.3 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 12.42 GPa
1801 ksi
50 mm/min; ASTM D 638
Flexural Strength 183 MPa
26500 psi
ISO 178
255 MPa
37000 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 10.78 GPa
1564 ksi
2 mm/min; ISO 178
10.79 GPa
1565 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 1.38 J/cm

@Temperature 23.0 °C
 2.59 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 11.21 J/cm

@Temperature 23.0 °C
 21.00 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 219 °C

@Thickness 3.20 mm
 426 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 214 °C
417 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
207 °C

@Thickness 3.20 mm
 405 °F

@Thickness 0.126 in
 unannealed; ASTM D 648