- Acrylonitrile Butadiene Styrene (ABS), Molded
- Chi Mei Polylac® PA-709 ABS
Chi Mei Polylac® PA-709 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Polylac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Polylac® PA-709 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Super impact
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 0.50 g/10 min @Load 5.00 kg, Temperature 200 °C |
0.50 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO-1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 102 | 102 | ASTM D785 |
| Ball Indentation Hardness | 86.0 MPa | 12500 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 55 % | 55 % | 50 mm/min; ISO 527 |
| Flexural Strength | 58.0 MPa | 8410 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.80 GPa | 261 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 4.10 J/cm @Thickness 6.35 mm |
7.68 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 4.65 J/cm @Thickness 3.17 mm |
8.71 ft-lb/in @Thickness 0.125 in |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | ISO 180/1C |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 3.20 J/cm² | 15.2 ft-lb/in² | ISO 179 |
| Impact | 21.0 | 21.0 | Impact Flexural Test Notched (KJ/m²) |
| NB | NB | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | unannealed; ISO 75 |
| 98.0 °C | 208 °F | annealed; ISO 75 | |
| Vicat Softening Point | 94.0 °C @Load 5.00 kg |
201 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 95.0 °C @Load 5.00 kg |
203 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 103 °C @Load 1.00 kg |
217 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 104 °C @Load 1.00 kg |
219 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- Raschig Group MELOPLAS® 182 MF
- Plaskolite West Optix® CA-75 General Purpose Acrylic Resin
- Silberline EternaBrite® Premier 251-DL
- Samsung Cheil Industries Starex® SL-0110 ABS, Unreinforced
- Shinkong Synthetic Fibers Shinite® D201 PBT
- Saint-Gobain Normount® V1300 White Polyurethane Foam Bonding Tape for Interior Use
- SABIC Innovative Plastics LNP VERTON UF-700-12 HS EXP PPA (Asia Pacific)
- DuPont Performance Polymers Zytel® 70G43HSLA BK099 Nylon 66 (Unverified Data**)
- Colorite Polymers 2018 Rigid PVC
Copyright © lookpolymers.com All Rights Reserved