Chi Mei Kibilac® PW-997S ASA Polymer

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer Chi Mei Corporation (ChiMei)
Trade Name Kibilac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Chi Mei Kibilac® PW-997S ASA Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Extrusion
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
ISO1183
Melt Flow 3.8 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 3.8 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 Melt Volume Rate (ml/10 min); ISO 1133
Mechanical Properties Metric English Comments
Ball Indentation Hardness 88.0 MPa
12800 psi
H358/30; ISO 2039-1
Tensile Strength at Break 42.0 MPa
6090 psi
50 mm/min; ISO 179/2D
Tensile Strength, Yield 48.0 MPa
6960 psi
50 mm/min; ISO 527
Elongation at Break 80 %
80 %
50 mm/min; ISO 527
Flexural Strength 65.0 MPa
9430 psi
2 mm/min; ISO 178
Flexural Modulus 1.80 GPa
261 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
ISO 180/1C
Charpy Impact Unnotched NB
NB
ISO 179
Charpy Impact, Notched 2.05 J/cm²
9.76 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 86.0 °C
187 °F
unannealed; ISO 75
96.0 °C
205 °F
annealed; ISO 75
Vicat Softening Point 92.0 °C

@Load 5.00 kg
 198 °F

@Load 11.0 lb
 50°C/hr; ISO 306
95.0 °C

@Load 5.00 kg
 203 °F

@Load 11.0 lb
 120°C/hr; ISO 306
105 °C

@Load 1.00 kg
 221 °F

@Load 2.20 lb
 50°C/hr; ISO 306
108 °C

@Load 1.00 kg
 226 °F

@Load 2.20 lb
 120°C/hr; ISO 306
Flammability, UL94 HB
HB
UL 94