- Toyobo VYLOPET® EMC330 Injection Molding Polyester Resin, Hydrolysis Resistant
Toyobo VYLOPET® EMC330 Injection Molding Polyester Resin, Hydrolysis Resistant
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Toyobo |
| Trade Name | VYLOPET® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo VYLOPET® EMC330 Injection Molding Polyester Resin, Hydrolysis Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Electric rice cooker partsBathroom appliancesFeatures: Good hydrolysis resistanceInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | MD |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 190 MPa | 27600 psi | ASTM D790 |
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 15 | 15 | CS-17; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 255 °C | 491 °F | By DSC |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Provisional 150, Thermal index; ASTM UL746B |
| 225 °C | 437 °F | Ball pressure temperature; IEC Method | |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.7937 mm |
HB @Thickness 0.03125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 131 sec | 131 sec | UL recognition value, tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 175 - 249 V | 175 - 249 V | IEC Pub1.112, class 3; IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 255 - 270 °C | 491 - 518 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F |
Users viewing this material also viewed the following:
- S&E Specialty Polymers XP44-10MG PVC
- Eastman 5220 LDPE 6% VA Copolymer, High Clarity, Ultra-High Impact Film Resin (discontinued **)
- IBC Advanced Alloys 4% BeCu Beryllium Copper Master Alloy
- Samsung Cheil Industries Infino® NF-3017H PC/ABS, Unreinforced FR
- Polyram PlusTek PA303G5 Nylon 6.6, 25% Glass Fiber
- ExxonMobil Santoprene® 141-55W185 Thermoplastic Elastomer (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved