Dow DOWLEX™ 2267G Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2267G Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A high performance stretch film resin Complies with U.S. FDA 21 CFR 177.1520 (c) 3.1a Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 9.218 MPa | 1337 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.501 MPa | 1378 psi | ASTM D882 |
| Film Elongation at Break, MD | 421 % | 421 % | ASTM D882 |
| Film Elongation at Break, TD | 608 % | 608 % | ASTM D882 |
| Secant Modulus, MD | 0.1494 GPa | 21.67 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.15536 GPa | 22.533 ksi | 2% Secant; ASTM D882 |
| Impact | 130 | 130 | [ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method |
| 765 | 765 | [ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882 | |
| 918 | 918 | [ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 323 g | 323 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 518 g | 518 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 15.896 g/micron | 403.75 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 25.49 g/micron | 647.5 g/mil | ASTM D1922 |
| Dart Drop Test | 474 g | 1.05 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 33.34 MPa | 4835 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.66 MPa | 3722 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 65 % | 65 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- MetalTek J92180 17-4 PH® Precipitation Hardening Steel
- Kraton® G1660 H (SEBS) Linear Triblock Copolymer
- Heatbath/Park Durastrip 1500 Cleaning Salt
- Techmer ES HiFill® PBT 613
- Unifrax PC Series™ PC Max™ Paper Ceramic Fiber Filtration Media
- American Elements Copper Oxide Nanopowder
- Chosun Refractories AB10S Alumina Magnesia Carbon Bricks for Ladle Wall And Bottom
- XXXPC Phenolic Laminate
- Huntsman PE2049 Injection Molding Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved