- Special Metals NIMONIC® Alloy 105
Special Metals NIMONIC® Alloy 105
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | NIMONIC® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals NIMONIC® Alloy 105.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A precipitation-hardenable nickel-cobalt-chromium alloy with an addition of molybdenum for solid-solution strengthening. The relatively high aluminum content enhances both strength (through greater precipitation hardening) and oxidation resistance. The alloy has high creep-rupture properties at temperatures to about 1740°F (950°C). Used in gas turbines for blades, discs, and shafts. Standard product forms are round and extruded section.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.01 g/cc | 0.289 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1030 MPa @Temperature 650 °C |
149000 psi @Temperature 1200 °F |
Precipitation Hardened prior to test |
| 1150 MPa @Temperature 23.0 °C |
167000 psi @Temperature 73.4 °F |
||
| Tensile Strength, Yield | 770 MPa @Strain 0.200 % |
112000 psi @Strain 0.200 % |
Precipitation Hardened. Value at room temperature |
| 720 MPa @Strain 0.200 %, Temperature 650 °C |
104000 psi @Strain 0.200 %, Temperature 1200 °F |
Precipitation Hardened prior to test | |
| Elongation at Break | 25 % | 25 % | Precipitation Hardened |
| 30 % @Temperature 650 °C |
30 % @Temperature 1200 °F |
Precipitation Hardened prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.2 µm/m-°C @Temperature 20.0 - 100 °C |
6.78 µin/in-°F @Temperature 68.0 - 212 °F |
|
| Specific Heat Capacity | 0.419 J/g-°C | 0.100 BTU/lb-°F | |
| Thermal Conductivity | 10.89 W/m-K | 75.58 BTU-in/hr-ft²-°F | |
| Melting Point | 1290 - 1345 °C | 2350 - 2453 °F | |
| Solidus | 1290 °C | 2350 °F | |
| Liquidus | 1345 °C | 2453 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | 4.5 - 4.9 % | 4.5 - 4.9 % | |
| Boron, B | 0.0030 - 0.010 % | 0.0030 - 0.010 % | |
| Carbon, C | <= 0.12 % | <= 0.12 % | |
| Chromium, Cr | 14 - 15.7 % | 14 - 15.7 % | |
| Cobalt, Co | 18 - 22 % | 18 - 22 % | |
| Copper, Cu | <= 0.20 % | <= 0.20 % | |
| Iron, Fe | <= 1.0 % | <= 1.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 4.5 - 5.5 % | 4.5 - 5.5 % | |
| Nickel, Ni | 51 % | 51 % | As remainder |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Titanium, Ti | 0.90 - 1.5 % | 0.90 - 1.5 % | |
| Zirconium, Zr | <= 0.15 % | <= 0.15 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000131 ohm-cm | 0.000131 ohm-cm | |
| Magnetic Permeability | 1.0007 | 1.0007 | at 200 oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® H&T CLH 150 Linear Low Density Polyethylene
- Pacific Sintered Materials FN-253-S(HT) 4600 Powdered Metal
- LG Chemical LUMID GP2251BF PA66+GF25%, Flame Retardant
- Techmer ES Luriblend® PA6/6 GF30 TL5 LE 30% Glass Filled
- CeramTec SL 303 Silicon Nitride, SiAION+SiC
- Westlake Tymax™ GA7001 Anhydride Modified Acrylate Copolymer (Developmental)
- Loctite® 3103 Acrylic Light Cure Adhesive
- 3M FP082 Clear Polypropylene Label Products
- 3M GLS100 Glossy Protection Film
- Solvay RHODAPEX® CD-128 Surfactant
Copyright © lookpolymers.com All Rights Reserved