- Chase Plastics CP Pryme® NN343L (Dry) Nylon 66, 43% Glass Fiber Reinforced, Lubricated, Recycled Content
Chase Plastics CP Pryme® NN343L (Dry) Nylon 66, 43% Glass Fiber Reinforced, Lubricated, Recycled Content
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® NN343L (Dry) Nylon 66, 43% Glass Fiber Reinforced, Lubricated, Recycled Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Recycled contentForm: PelletsInformation provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Filler Content | 43 % | 43 % | |
| Water Absorption | 0.80 % | 0.80 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 100 | 100 | ASTM D785 |
| Tensile Strength at Break | 200 MPa | 29000 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 303 MPa | 44000 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Fainplast Compounds RK 320 Rigid PVC, Extrusion Lead Free
- Momentive Performance Materials NX5 Boron Nitride (BN) Powder
- H.C. Starck Amperit® 105.2 Agglomerated Sintered Molybdenum (Mo)
- Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes
- SABIC Innovative Plastics Valox® 365 PC+PET
- Techmer ES Luriblend® PA6 ML2 HS BK Nylon 6
- American Elements Rhenium Nanoparticles
- Arlon R30711R020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3M 06396 Adhesion Promoter
- Multibase Multi-Flex® TPE A 5703 BLK Low AO
Copyright © lookpolymers.com All Rights Reserved