Arkema Group Rilsan® AMN D Nylon 12, Rigid, Injection Grade (Conditioned)

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	Arkema
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Rilsan® AMN D Nylon 12, Rigid, Injection Grade (Conditioned).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Designation ISO 1874-PA12,MR,14-010Rigid grade for injection molding. Available colors: black, natural, orange, red and white. Possibilities of heat and light stabilizing agents. Mold-release agent.Good mechanical properties. Low friction coefficient. Easy filling of the mold due to its well adapted melt viscosity. Low shrinkage: include 1% on average for the design of the mold. Very good dimensional stability (low moisture absorption). High rate of production.UL classification: UL94 V2 (3,05mm) RTI(C) 65/65/65Example applications: Stressed mechanical parts in all industrial field.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.01 g/cc	0.0365 lb/in³
Melt Flow	69.4 g/10 min @Load 2.16 kg, Temperature 235 °C	69.4 g/10 min @Load 4.76 lb, Temperature 455 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	39.0 MPa	5660 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal Strain; 50 mm/min
Elongation at Yield	10 %	10 %	50 mm/min
Tensile Modulus	1.17 GPa	170 ksi	1 mm/min
Charpy Impact Unnotched	NB	NB
	NB	NB	Low Temp
Charpy Impact, Notched	0.610 J/cm²	2.90 ft-lb/in²
	0.590 J/cm² @Temperature -30.0 °C	2.81 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	130 µm/m-°C @Temperature 20.0 °C	72.2 µin/in-°F @Temperature 68.0 °F
CTE, linear, Transverse to Flow	120 µm/m-°C @Temperature 20.0 °C	66.7 µin/in-°F @Temperature 68.0 °F
Melting Point	174 °C	345 °F	(Dry)
Deflection Temperature at 0.46 MPa (66 psi)	135 °C	275 °F
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F
Vicat Softening Point	142 °C	288 °F	50°C/hr; 50N
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in
	V-2 @Thickness 3.20 mm	V-2 @Thickness 0.126 in
Oxygen Index	21 %	21 %

Electrical Properties	Metric	English
Electrical Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Strength	30.0 kV/mm	762 kV/in
Comparative Tracking Index	600 V	600 V