Loxim 821 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Talc Filler , Polypropylene, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 821 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.00 - 1.10 g/cc | 1.00 - 1.10 g/cc | ASTM D792 |
| Filler Content | 20 % | 20 % | |
| Linear Mold Shrinkage | 0.010 - 0.012 cm/cm | 0.010 - 0.012 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 26.0 - 28.0 MPa | 3770 - 4060 psi | ASTM D683 |
| Flexural Modulus | 1.80 - 2.00 GPa | 261 - 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 - 0.700 J/cm | 0.937 - 1.31 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 105 - 110 °C | 221 - 230 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Oxford Polymers Oxnilon 6-50GF 50% Glass Fiber Filled Nylon 6 for Injection Molding
- Polymer Resources NY66-IM1-G33-[color]-H Nylon 66, 33% Glass Reinforced, Toughened and Heat Stabilized
- 3M Dyneon™ Aflas® FA-150L PTFE Fluoroelastomer (discontinued **)
- MarkeTech Cu/Mo/Cu 1:3:1 Laminated Sheet
- Kotec Carbotex K-30UVR Polycarbonate, General Purpose, UV Stability + Mold Release Grade
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.015" thick)
- Teknor Apex Sinvicomp SRF 3707 Polyvinyl Chloride, Rigid
- Colorite Polymers 8312 Clear Injection Molding Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved