- Chase Plastics CP Pryme® N330L (Dry) Nylon 6, 30% Glass Fiber Reinforced, Lubricated, Recycled Content
Chase Plastics CP Pryme® N330L (Dry) Nylon 6, 30% Glass Fiber Reinforced, Lubricated, Recycled Content
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Chase Plastics |
| Trade Name | CP Pryme® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chase Plastics CP Pryme® N330L (Dry) Nylon 6, 30% Glass Fiber Reinforced, Lubricated, Recycled Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: LubricatedRecycled contentForm: PelletsInformation provided by Chase Plastics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 1.4 % | 1.4 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 165 MPa | 24000 psi | ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Flexural Strength | 255 MPa | 37000 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 1.01 J/cm | 1.90 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Intol® 1783 Emulsion Styrene-Butadiene Rubber
- Permabond 2010 Cyanoacrylate, gap filling
- Lubrizol Advanced Materials PEARLTHANE® 12K92A Thermoplastic Polyurethane Elastomer (discontinued **)
- Kazanorgsintez 102-15 Composition of Low Density Polyethylene, Crack-Proof
- Lehmann & Voss LUVOCOM® 1-0936 Polyamide 66, with glass fiber and PTFE, 8-mm-granulate
- Techmer ES HiFill® PA6 GF33 UG HS BK 33% Glass Filled
- ExxonMobil LD 051.LQ Shrink Film Resin
- Asia International Enterprise (Hong Kong) 60G8 Nylon 66, 40% Filled
- Bhansali Engineering Abstron IM-17A(DLW) ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved