SABIC Innovative Plastics GELOY XTWE265 ASA (Asia Pacific)

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY XTWE265 ASA (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Highly weatherable Geloy ASA profile extrusion grade for processes with simple or no calibration hardware.
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.55 %
0.55 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 5.2 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 5.2 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Melt Index of Compound 5.0 g/10 min

@Load 5.00 kg,
Temperature 220 °C
 5.0 g/10 min

@Load 11.0 lb,
Temperature 428 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 29.0 MPa
4210 psi
Type I, 50 mm/min; ASTM D638
29.0 MPa
4210 psi
50 mm/min; ISO 527
Tensile Strength, Yield 37.0 MPa
5370 psi
50 mm/min; ISO 527
38.0 MPa
5510 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 37 %
37 %
Type I, 50 mm/min; ASTM D638
40 %
40 %
50 mm/min; ISO 527
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527
4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 1.87 GPa
271 ksi
5 mm/min; ASTM D638
1.90 GPa
276 ksi
1 mm/min; ISO 527
Flexural Yield Strength 53.0 MPa
7690 psi
2 mm/min; ISO 178
56.0 MPa
8120 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 1.88 GPa
273 ksi
1.3 mm/min, 50 mm span; ASTM D790
1.90 GPa
276 ksi
2 mm/min; ISO 178
Izod Impact, Notched 2.60 J/cm
4.87 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 26.0 kJ/m²
12.4 ft-lb/in²
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.80 J/cm²
8.57 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 35.0 J

@Temperature 23.0 °C
 25.8 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 120 µm/m-°C

@Temperature -40.0 - 40.0 °C
 66.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
120 µm/m-°C

@Temperature -40.0 - 40.0 °C
 66.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 130 µm/m-°C

@Temperature -40.0 - 40.0 °C
 72.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
130 µm/m-°C

@Temperature -40.0 - 40.0 °C
 72.2 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 84.0 °C

@Thickness 3.20 mm
 183 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 82.0 °C
180 °F
Rate B/50; ASTM D1525
85.0 °C
185 °F
Rate B/50; ISO 306
87.0 °C
189 °F
Rate B/120; ISO 306