Ineos Styrenics Avantra® 2710 High Impact Styrenic Polymer (Global)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Styrenics |
| Trade Name | Avantra® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Styrenics Avantra® 2710 High Impact Styrenic Polymer (Global).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Avantra® 2710 is a high-impact grade of polystyrene with improved stress crack resistance, developed primarily for extrusion and thermoforming applications, especially for the refrigerator industry.Information provided by BASF.Ineos Styrenics purchased this product line from BASF in 2005.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | <= 0.10 % | <= 0.10 % | 23°C/50% RH |
| Water Absorption at Saturation | <= 0.10 % | <= 0.10 % | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 2.6 g/10 min @Load 5.00 kg, Temperature 200 °C |
2.6 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 42 | 42 | ASTM D785 |
| Tensile Strength at Break | 23.0 MPa | 3340 psi | ASTM D638 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ASTM D638 |
| Elongation at Break | 65 % | 65 % | ASTM D638 |
| Tensile Modulus | 1.655 GPa | 240.0 ksi | ASTM D638 |
| Flexural Modulus | 1.38 GPa | 200 ksi | ASTM D790-1 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | ASTM D256-A |
| Gardner Impact | 20.3 J @Thickness 3.17 mm, Temperature 23.0 °C |
15.0 ft-lb @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB | CSA 0.6 1.47 mm, Natural |
| HB @Thickness 1.10 mm |
HB @Thickness 0.0433 in |
White |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 10 % | 10 % | 60°; ASTM D523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.30e+13 ohm-cm | 1.30e+13 ohm-cm | ASTM D257 |
| Dielectric Strength | 44.4 kV/mm | 1130 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Extrusion |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1/TF/18/SI/2/BK Polyamide 66, with PTFE, lubricant modified, heat stabilized
- MetalTek MTEK 31 UNS R30031 Cobalt Base Alloy
- LATI Latilub 45/7-20T HDPE, PTFE Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP RP004 PA6.6 (Europe-Africa-Middle East)
- Teknor Apex ELEXAR® EL 8623 Thermoplastic Elastomer
- Lubrizol Stat-Rite® S-250 Static Control Polypropylene
- Wellman Wellamid® GF33-66 XE-N, 33% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized
- CP-Polymer-Technik Wellamid® 6000 MRGV 25/15 HWUVCP 25% Mineral and 15% Glass Fiber Nylon 6, UV Stabilized, Heat Stabilized, Conditioned
- Eurostar Staramide AG7H PA66, 35% Glass Filled, Injection Molded
- 3M 7033 Screen Printable Polyester Performance LabelProducts
Copyright © lookpolymers.com All Rights Reserved