SABIC Innovative Plastics LNP THERMOCOMP PFB91S PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PFB91S PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PFB91S is a compound based on Nylon 6 resin containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.0 MPa | 8990 psi | Type I, 5 mm/min; ASTM D638 |
| 62.0 MPa | 8990 psi | ASTM D638 | |
| Elongation at Break | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 |
| 2.7 % | 2.7 % | ASTM D638 | |
| Tensile Modulus | 7.49 GPa | 1090 ksi | 50 mm/min; ASTM D638 |
| Flexural Modulus | 6.04 GPa | 876 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.04 GPa | 876 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C @Thickness 3.20 mm |
325 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Pasargad Polymer Peyvand Pasamid 3P-H2000B1 Nylon 66
- Indium Corp. Indalloy 139 Lead Free Solder Alloy
- Saint-Gobain CHR® A603 Aluminum Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics Noryl PPX PPX615 PPE+PP
- Trelleborg Emerson & Cuming Syntac® 350 Composite Materials Syntactic Foam
- A. Schulman POLYBLAK™ 4663 Premium Conductive 40% Carbon Black Concentrate Based In Modified HDPE
- Elektro-Isola G-Etronax SI Silicone, Glass Fabric Reinforcement, White, Tubes
- 3M Scotchcal™ 1000-17 Graphic Film
- Fibre Glast 1110 CC Vinyl Ester Resin (Casting Properties) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved