CP-Polymer-Technik Wellamid® 6000 GVS 20/10 HWCP 20% Glass Fiber and 10% Glass Sphere Nylon 6, Heat Stabilized, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6000 GVS 20/10 HWCP 20% Glass Fiber and 10% Glass Sphere Nylon 6, Heat Stabilized, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.8 - 2.3 % | 1.8 - 2.3 % | 23°C/50%RH, Starting when dry; DIN 53495 |
| Linear Mold Shrinkage | 0.0050 cm/cm @Thickness 4.00 mm |
0.0050 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 4.00 mm |
0.0070 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 10 % | 10 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 5.00 GPa | 725 ksi | ISO 527 |
| Charpy Impact Unnotched | 9.50 J/cm² @Temperature 23.0 °C |
45.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 1.80 J/cm² @Temperature 23.0 °C |
8.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | Kofler |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | ISO 3915 |
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz |
7.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.10 | 0.10 | At 1 MHz; IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | High | |
| Screw Speed | High |
Users viewing this material also viewed the following:
- REXtac Rextac® RT 2304 Amorphous Polyalphaolefin (APAO)
- Hogen HM3750 Tungsten-Based Metal
- Lehmann & Voss LUVOCOM® 1-8379 Polyamide 66, with PTFE
- SABIC Innovative Plastics ULTEM 1010TC PEI (Asia Pacific)
- Teknor Apex Telcar® OBC 4555A Thermoplastic Elastomer
- A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- Beijing Ranger Chem PBT-MFC-101G30 FR PBT
- BASF Ultramid® SEG7 35% Glass Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved