SABIC Innovative Plastics LNP STAT-LOY M3000C PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Stat-loy |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-LOY M3000C PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-LOY* M3000C is a compound based on unfilled Polypropylene resin. Added features of this grade include: Clean Compound System, Antistat.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 |
| 0.930 g/cc | 0.0336 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.160 % | 0.160 % | 50% RH, 24 hrs; ASTM D570 |
| 0.160 % | 0.160 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.020 cm/cm @Time 86400 sec |
0.010 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 18.0 MPa | 2610 psi | Type I, 5 mm/min; ASTM D638 |
| 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 689 % | 689 % | Type I, 5 mm/min; ASTM D638 |
| 690 % | 690 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 0.760 GPa | 110 ksi | 50 mm/min; ASTM D638 |
| 1.18 GPa | 171 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 24.0 MPa | 3480 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 38.0 MPa | 5510 psi | ISO 178 | |
| Flexural Modulus | 0.860 GPa | 125 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.96 GPa | 284 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.750 J/cm | 1.41 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 29.0 J @Temperature 23.0 °C |
21.4 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 25.0 J | 18.4 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 128 µm/m-°C @Temperature -30.0 - 30.0 °C |
71.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 131 µm/m-°C @Temperature -30.0 - 30.0 °C |
72.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 74.0 °C @Thickness 3.20 mm |
165 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 49.0 °C @Thickness 3.20 mm |
120 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+10 - 1.00e+12 ohm | 1.00e+10 - 1.00e+12 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Polymer Resources NY66-IM2-[color]-H Impact Modified Nylon 66, Heat Stabilized
- PolyOne Geon™ HC 2175G Polyvinyl Chloride, Flexible (PVC, Flexible)
- DSM Akulon® K224-HG3 Nylon 6-15% Glass Reinforced (European and Asian Grade) (Dry)
- Epoxy Technology EPO-TEK® 302-3M Optically Transparent Epoxy
- DuPont Teijin Films Melinex® 194 Polyester Film, 380 Gauge
- Eurotec® Tecodur® PB70 GR50 BK009 MX01 PBT/PET, 50% glass fiber reinforced, heat & UV stabilized, improved impact, natural
- Bapolan® 6409 Polystyrene, Injection Grade
- Armstrong A-12-T Epoxy Adhesive
- Asahi Kasei Thermylene® P6-30FG-0600R 30% Glass Fiber Reinforced, Heat Stabilized
- Karina E 842-18/106-Y-RT-POWDER Compound PVC Gray
Copyright © lookpolymers.com All Rights Reserved