- CP-Polymer-Technik Wellamid® 6000 GV 35 HWCP 35% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
CP-Polymer-Technik Wellamid® 6000 GV 35 HWCP 35% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | CP-Polymer-Technik GmbH & Co. |
| Trade Name | Wellamid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CP-Polymer-Technik Wellamid® 6000 GV 35 HWCP 35% Glass Fiber Nylon 6, Heat Stabilized, Conditioned.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by CP-Polymer-Technik GmbH & Co. KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.8 - 2.3 % | 1.8 - 2.3 % | 23°C/50%RH, Starting when dry; DIN 53495 |
| Linear Mold Shrinkage | 0.0020 cm/cm @Thickness 4.00 mm |
0.0020 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 4.00 mm |
0.0080 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.20 GPa | 1040 ksi | ISO 527 |
| Charpy Impact Unnotched | 11.0 J/cm² @Temperature 23.0 °C |
52.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | Kofler |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | ISO 3915 |
| Dielectric Constant | 7.0 @Frequency 1e+6 Hz |
7.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 243-1 |
| Dielectric Loss Index | 0.20 | 0.20 | At 1 MHz; IEC 250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Holding Pressure | High | |
| Injection Speed | Medium to High | |
| Screw Speed | High |
Users viewing this material also viewed the following:
- LNP Lubricomp® EFL-4544 Polyetherimide, Glass Fiber Reinforcement, PTFE Lubricant (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP RAL23S PA 66 (Asia Pacific)
- Styrolution Polystyrol 158 K GR 21 PS
- Teknor Apex Monprene® MP-1791R4 Thermoplastic Elastomer
- Shin-Etsu Silicones KF-9909 Fluid
- Solvay RHODASURF® L-7/90 Surfactant
- Eurostar Starpylen MF007AS PP, Glass Fiber Filled, Injection Molded
- DuPont Teijin Films Teonex® Q72 Polyester Film, 14 Gauge
- BASF Polystyrol® 475 K Impact Grade Polystyrene (Europe)
- Formosa Plastics Formolene® LH5212 Injection Molding HDPE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved