Addiplast Addilene H 490 M40F Flame Retardant Polypropylene, 40% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant , Polypropylene, Mineral Reinforced |
| Manufacturer | Addiplast |
| Trade Name | Addilene |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addilene H 490 M40F Flame Retardant Polypropylene, 40% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant, mineral filled, with halogensInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183/A |
| Melt Flow | 10 g/10 min | 10 g/10 min | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 78 | 78 | Conditioned; ISO 868 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | Conditioned; ISO R 527 |
| Elongation at Break | 5.0 % | 5.0 % | Conditioned; ISO R 527 |
| Modulus of Elasticity | 4.20 GPa | 609 ksi | Conditioned; ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | Conditioned; ISO 180/1A |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | Conditioned; ISO 179/IeU |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 168 °C | 329 - 334 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-2/AF |
| Vicat Softening Point | 153 °C | 307 °F | ISO 306/A50 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Oxygen Index | 27 % | 27 % | ISO 4589 |
| Glow Wire Test | 960 °C | 1760 °F | CEI 60695/2/1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | Conditioned; CEI 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | Conditioned; CEI 60093 |
| Dielectric Strength | 42.0 kV/mm | 1070 kV/in | CEI 60243-1 |
| Comparative Tracking Index | >= 600 V | >= 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8510 (487) (UF) Synthetic Oil
- Samsung Cheil Industries Infino® GP-8200G MPPE, 20% Glass Filled
- Samsung Cheil Industries Starex® VG-4910 ABS, Glass Filled FR
- SABIC Innovative Plastics LNP THERMOCOMP QC006 PA6.10 (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP THERMOCOMP RF0059 PA 66
- Borealis Casico™ FR4805 Non Halogen Flame Retardant Compound for Sheathing Energy Cables
- Eastman Cadence™ GS4 Copolyester for film calendering
- 3M 365 Thermosetable Glass Cloth Tape
- 3M 465 Splicing Tapes
- Covestro Makrofol® ID 6-2 Polycarbonate
Copyright © lookpolymers.com All Rights Reserved