CENTROPLAST CENTROLEN PPS Polypropylene flame resistant

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer	CENTROPLAST Engineering Plastics GMBH
Trade Name	CENTROLEN
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	CENTROPLAST CENTROLEN PPS Polypropylene flame resistant.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This material is a low density, easily machined plastic that can be welded and is flame resistant. Applications include exhaust systems for heating systems, and apparatus engineering.Information provided by CENTROPLAST Engineering Plastics GMBH

Physical Properties	Metric	English	Comments
Density	0.920 g/cc	0.0332 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	62.0 MPa	8990 psi	value at 30 sec.; ISO 2039-1
Tensile Strength, Yield	30.0 MPa	4350 psi	v = 50 mm/min; ISO 527-2
Elongation at Break	10 %	10 %	ISO 527-2
Tensile Modulus	1.30 GPa	189 ksi	ISO 527-2
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm²	4.76 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.170 W/m-K	1.18 BTU-in/hr-ft²-°F
Melting Point	165 °C	329 °F	10K/min; ISO 3146
Maximum Service Temperature, Air	100 °C	212 °F	Long Term
	130 °C	266 °F	Short term
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F	ISO 75-2
Vicat Softening Point	85.0 °C	185 °F	VST/B/50; ISO 306
Flammability, UL94	V-2 @Thickness 3.00 mm	V-2 @Thickness 0.118 in
	V-2 @Thickness 6.00 mm	V-2 @Thickness 0.236 in

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+14 ohm-cm	1.00e+14 ohm-cm	IEC 60093
Surface Resistance	1.00e+15 ohm	1.00e+15 ohm	IEC 60093
Dielectric Constant	2.3 @Frequency 1e+6 Hz	2.3 @Frequency 1e+6 Hz	IEC 60250
Dissipation Factor	0.0012 @Frequency 1e+6 Hz	0.0012 @Frequency 1e+6 Hz	IEC 60250
Comparative Tracking Index	600 V	600 V	IEC 60112