Techmer ES Electrablend® PPS 05002
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler , Polyphenylene Sulfide (PPS), Conductive |
| Manufacturer | Techmer ES |
| Trade Name | Electrablend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES Electrablend® PPS 05002.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber ReinforcementFeatures: Electrically ConductiveInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ASTM D792 |
| Water Absorption | 0.050 % @Time 86400 sec |
0.050 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm |
0.0040 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Yield | 165 MPa | 24000 psi | ASTM D638 |
| Elongation at Break | 1.7 % | 1.7 % | ASTM D638 |
| Flexural Strength | 228 MPa | 33000 psi | ASTM D790 |
| Flexural Modulus | 13.1 GPa | 1900 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm |
0.900 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.8 µm/m-°C | 11.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 274 °C | 525 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 10 - 1000 ohm-cm | 10 - 1000 ohm-cm | ASTM D257 |
| Surface Resistance | 10 - 1000 ohm | 10 - 1000 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- LG Chemical Lupox® GP-2301F General Purpose PBT, 30% Glass Fiber Reinforced, Flame Retardant
- Ipiranga Petrochem LB 0216 LLDP
- Solvay TECHNYL® eXten D218 V30 Nylon 6.10, 30% glass fiber, DRY
- SABIC Innovative Plastics ULTEM HU1000 PEI (Asia Pacific)
- Plenco 2311 Phenolic, Granular, Injection Molded
- Wall Colmonoy COLMONOY® 5 PTA - Nickel-Base Hard Surfacing Alloy With Chromium Boride
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 50A, Non-Black Peroxide Cure
- A. Schulman ComAlloy E-16674B PPS, Electrically Conductive - Carbon Fiber Filled
- Nye Lubricants 200RP (SO) Synthetic Oil
- Samyang Triel® 5550 Thermoplastics Polyetherester Elastomer, General Extrusion
Copyright © lookpolymers.com All Rights Reserved