LATI Larton GCE/650 PPS, Glass/Mineral Reinforced

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Mineral/Glass-Fiber Filled
Manufacturer LATI
Trade Name Larton
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Larton GCE/650 PPS, Glass/Mineral Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyphenylene Sulfide (PPS) based compound. Glass fibers / Mineral filler. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.97 g/cc
0.0712 lb/in³
Linear Mold Shrinkage, Flow 0.0010 - 0.0020 cm/cm
0.0010 - 0.0020 in/in
Linear Mold Shrinkage, Transverse 0.0015 - 0.0030 cm/cm
0.0015 - 0.0030 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa

@Temperature 150 °C
 13100 psi

@Temperature 302 °F
105 MPa

@Temperature 120 °C
 15200 psi

@Temperature 248 °F
125 MPa

@Temperature 90.0 °C
 18100 psi

@Temperature 194 °F
145 MPa

@Temperature 60.0 °C
 21000 psi

@Temperature 140 °F
165 MPa

@Temperature 23.0 °C
 23900 psi

@Temperature 73.4 °F
Elongation at Break 0.80 %

@Temperature 23.0 °C
 0.80 %

@Temperature 73.4 °F
0.90 %

@Temperature 60.0 °C
 0.90 %

@Temperature 140 °F
1.0 %

@Temperature 90.0 °C
 1.0 %

@Temperature 194 °F
1.6 %

@Temperature 120 °C
 1.6 %

@Temperature 248 °F
2.3 %

@Temperature 150 °C
 2.3 %

@Temperature 302 °F
Tensile Modulus 9.40 GPa

@Temperature 150 °C
 1360 ksi

@Temperature 302 °F
14.2 GPa

@Temperature 120 °C
 2060 ksi

@Temperature 248 °F
20.8 GPa

@Temperature 90.0 °C
 3020 ksi

@Temperature 194 °F
22.0 GPa

@Temperature 60.0 °C
 3190 ksi

@Temperature 140 °F
23.0 GPa

@Temperature 23.0 °C
 3340 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 1.50 J/cm²
7.14 ft-lb/in²
Charpy Impact, Notched 0.550 J/cm²
2.62 ft-lb/in²
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 225 °C
437 °F
Deflection Temperature at 0.46 MPa (66 psi) 285 °C
545 °F
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
Vicat Softening Point 260 °C

@Load 5.00 kg
 500 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 45 %
45 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 150 V
150 V
A solution
Processing Properties Metric English Comments
Melt Temperature 290 - 330 °C
554 - 626 °F
Mold Temperature 130 - 140 °C
266 - 284 °F
Drying Temperature 130 - 150 °C

@Time 10800 sec
 266 - 302 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa