Borealis Daplen™ EE103AE TPO Compound

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO) , Polypropylene (PP) , TPO
Manufacturer Borealis
Trade Name Daplen™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Daplen™ EE103AE TPO Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Daplen EE103AE is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. Daplen EE103AE is a material with excellent impact /stiffness ratio. Thanks to its low thermal expansion this material is suitable to mold parts requiring low change of dimensions over a broad temperature range. This product is optimized to give good surface aesthetics.Daplen EE103AE has been developed especially for bumpers and exterior trims.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.950 g/cc
0.0343 lb/in³
ISO 1183
Linear Mold Shrinkage 0.010 cm/cm
0.010 in/in
Borealis Method
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 230 °C
12 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 18.0 MPa
2610 psi
At 50 mm/min; ISO 527-2
Elongation at Break 60 %
60 %
At 50 mm/min; ISO 527-2
Elongation at Yield 5.0 %
5.0 %
At 50 mm/min; ISO 527-2
Tensile Modulus 1.40 GPa
203 ksi
At 1 mm/min; ISO 527-2
Flexural Strength 24.5 MPa
3550 psi
ISO 178
Flexural Modulus 1.50 GPa
218 ksi
At 2 mm/min; ISO 178
Izod Impact, Notched (ISO) 35.0 kJ/m²
16.7 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
ISO 179/1eU
Charpy Impact, Notched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 67.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
37.2 µin/in-°F

@Temperature -22.0 - 176 °F
Borealis Method
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C
198 °F
ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75-2
Vicat Softening Point 45.0 °C
113 °F
B (50N); ISO 306
Shrinkage 0.150 %

@Temperature 90.0 °C,
Time 7200 sec
0.150 %

@Temperature 194 °F,
Time 2.00 hour
Post Shrinkage; Borealis Method
Processing Properties Metric English Comments
Melt Temperature 220 - 260 °C
428 - 500 °F
Polymer Mass Temp
Mold Temperature 30.0 - 50.0 °C
86.0 - 122 °F