Global TPO-55D TPO Grade
| Category | Polymer , Thermoplastic , TPO |
| Manufacturer | Global Polymers Corporation |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Global TPO-55D TPO Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Global Polymers Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 55 | 55 | ASTM D2240 |
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | ASTM D638 |
| Flexural Modulus | 0.586 GPa | 85.0 ksi | ASTM D790 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 115-25 Ground Alumina
- Palm Labs Adhesives Turbo Fuse Series 440 (GEL) Rapid Bonding Adhesive
- Polymer Resources PPX-GP4 Modified PPO, General Purpose with HDT of 210 F (Unverified Data**)
- JPJ Technologies 6600B HDPE Blow Molding
- Haynes R-41 alloy, 0.635 mm thick sheet, solution heat treated at 1079°C, water quenched, 30 minutes at 1066°C, aged 16 hours at 760°C (1400°F), air cooled
- Schott Glass 8100 Lead Glass
- Schott N-LAF35 Glass
- Westlake EB591 9.0% Ethylene Vinyl Acetate Copolymer
- Cytec Thornel® T-605/50X 12K Carbon Fiber, Polyacrylonitrile (PAN) Precursor
- Overview of materials for Polyethylene Terephthalate (PET), 40% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved