Borealis Bormod™ HD905CF Polypropylene Homopolymer for Cast Film

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Borealis
Trade Name Bormod™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Borealis Bormod™ HD905CF Polypropylene Homopolymer for Cast Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Bormod HD905CF is a high crystallinity homopolymer film resin, based on special Borstar nucleating technology, suitable for the manufacturing of unoriented film on chill roll process. It is recommended to use rather high chill roll temperatures in the range of 40-55°C to obtain the optimum film stiffness. Optical properties will not be deteriorated as with conventional homopolymers at these temperatures.Bormod HD905CF is especially suitable for twist films, labeling films, lamination films, furniture films, decorating films, and textile films.Information provided by the Manufacturer.
Physical Properties Metric English Comments
Density 0.900 - 0.910 g/cc
0.0325 - 0.0329 lb/in³
ISO 1183
Melt Flow 8.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 80 %
80 %
ISO 527-3
Film Elongation at Break, TD 120 %
120 %
ISO 527-3
Flexural Modulus 2.10 GPa
305 ksi
ISO 178
Secant Modulus, MD 1.60 GPa
232 ksi
ISO 527-3
Secant Modulus, TD 1.80 GPa
261 ksi
ISO 527-3
Impact 40
40
Dynatest, Damaging Force (N); ISO 7765-2
Impact Test 0.950 J
0.701 ft-lb
Dynatest, Penetration Energy; ISO 7765-2
Coefficient of Friction 0.30 - 0.40
0.30 - 0.40
Film/Film; ISO 8295
Film Tensile Strength at Break, MD 35.0 - 55.0 MPa
5080 - 7980 psi
ISO 527-3
Film Tensile Strength at Break, TD 30.0 - 50.0 MPa
4350 - 7250 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 164 - 170 °C
327 - 338 °F
ISO 3146
Vicat Softening Point 158 °C
316 °F
A (10 N); ISO 306
Optical Properties Metric English Comments
Haze <= 6.0 %
<= 6.0 %
ASTM D1003
Gloss >= 90 %
>= 90 %
ASTM D2457