Palm Labs Adhesives TURBO-LOCK SERIES 17-OR Anaerobic Thread Locking Compound

Category	Polymer , Adhesive , Thermoset , Methacrylate , Methacrylate Adhesive
Manufacturer	Palm Labs Adhesives
Trade Name	TURBO-LOCK SERIES
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Palm Labs Adhesives TURBO-LOCK SERIES 17-OR Anaerobic Thread Locking Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BEARING AND SHAFT - SERIES 17-OR is a fast curing, GREEN, high strength, oil resistant, close fit, anaerobic retaining compound for bonding, sealing and retaining of cylindrical parts. It is highly resistance to heat, vibrations, water, gases, oils, hydrocarbons and many chemicals.Applications:Ideal to fill gaps up to 0.005”Excellent for slightly oil contaminated, close fitting parts.Withstands working temperatures up to 300ºFRetaining sleeves, pulleys, gears, rotors and fans on shafts.Mounting sleeves, securing bushings, bearings and plugs in housing.Excellent retaining and sealing compoundPart Numbers for this data: 17-001-OR, 17-010-OR, 17-050-OR, 17-250-OR, 17-1000-ORInformation provided by Palm Laboratories Adhesives

Physical Properties	Metric	English	Comments
Specific Gravity	1.10 g/cc	1.10 g/cc
Brookfield Viscosity	125 cP	125 cP	RVT Spindle 3 @ 20 rpm

Mechanical Properties	Metric	English	Comments
Shear Strength	13.0 - 15.0 MPa @Temperature 22.0 °C, Time 108000 sec	1890 - 2180 psi @Temperature 71.6 °F, Time 30.0 hour	ISO 10123; Compressive, Steel pins and collars
	20.0 - 32.0 MPa @Temperature 22.0 °C, Time 86400 sec	2900 - 4640 psi @Temperature 71.6 °F, Time 24.0 hour	ISO 10123; Compressive, Steel pins and collars

Thermal Properties	Metric	English	Comments
CTE, linear	0.800 µm/m-°C	0.444 µin/in-°F	ASTM D696
Specific Heat Capacity	0.300 J/g-°C	0.0717 BTU/lb-°F
Thermal Conductivity	0.100 W/m-K	0.694 BTU-in/hr-ft²-°F	ASTM C177
Flash Point	>= 33.9 °C	>= 93.0 °F

Processing Properties	Metric	English	Comments
Cure Time	120 - 240 min	2.00 - 4.00 hour	Functional
	1440 min	24.0 hour	Full
	25.00 - 30.0 min @Temperature -55.0 - 150 °C	0.4167 - 0.500 hour @Temperature -67.0 - 302 °F	Handling
Shelf Life	24.0 Month	24.0 Month

Descriptive Properties	Value	Comments
Appearance	Green
Chemical Resistance	100% Initial Strength Retained	Acetone at 22°C, at 500hrs
	100% Initial Strength Retained	Ethanol at 22°C, at 500hrs
	100% Initial Strength Retained	Motor Oil at 125°C, at 500hrs
	100% Initial Strength Retained	Gasoline at 22°C, at 500hrs
	100% Initial Strength Retained	Brake Fluid at 22°C, at 500hrs
	100% Initial Strength Retained	Ethanol at 22°C, at 1000hrs
	100% Initial Strength Retained	Motor Oil at 125°C, at 1000hrs
	100% Initial Strength Retained	Gasoline at 22°C, at 1000hrs
	100% Initial Strength Retained	Brake Fluid at 22°C, at 1000hrs
	85% Initial Strength Retained	Water/Glycol at 87°C, at 1000hrs
	90% Initial Strength Retained	Water/Glycol at 87°C, at 500hrs
	95% Initial Strength Retained	Acetone at 22°C, at 1000hrs
Composition	Urethane Methacrylate
Gap Fill	0.005"