Lubrizol Estane® 2355-80AE Thermoplastic Polyurethane Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade
Manufacturer Lubrizol (former Noveon)
Trade Name ESTANE®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lubrizol Estane® 2355-80AE Thermoplastic Polyurethane Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Formerly PellethaneFeature: Damping capacityAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0060 cm/cm
0.0050 - 0.0060 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0020 - 0.0060 cm/cm
0.0020 - 0.0060 in/in
ASTM D955
Melt Flow 7.0 g/10 min

@Load 8.70 kg,
Temperature 224 °C
7.0 g/10 min

@Load 19.2 lb,
Temperature 435 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 85
85
ASTM D2240
Tensile Strength, Ultimate 39.2 MPa
5690 psi
ASTM D412
Elongation at Break 550 %
550 %
ASTM D412
50% Modulus 0.00386 GPa
0.560 ksi
ASTM D412
100% Modulus 0.00620 GPa
0.899 ksi
ASTM D412
300% Modulus 0.0152 GPa
2.20 ksi
ASTM D412
Tear Strength 126 kN/m
719 pli
ASTM D624
Taber Abrasion, mg/1000 Cycles 10
10
H22 Wheel, 1000g; ASTM D1044
Compression Set 25 %

@Temperature 25.0 °C,
Time 79200 sec
25 %

@Temperature 77.0 °F,
Time 22.0 hour
ASTM D395, Method B
75 %

@Temperature 70.0 °C,
Time 79200 sec
75 %

@Temperature 158 °F,
Time 22.0 hour
ASTM D395, Method B
Tensile Set 60 %
60 %
Elongation set after break; ASTM D412
Thermal Properties Metric English Comments
CTE, linear 166 µm/m-°C

@Temperature 20.0 °C
92.2 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Vicat Softening Point 93.0 °C
199 °F
120°C/hr, 9.8N; ASTM D1525
Glass Transition Temp, Tg -37.0 °C
-34.6 °F
DSC
Processing Properties Metric English Comments
Melt Temperature 188 - 204 °C
370 - 399 °F
Extrusion
193 - 204 °C
379 - 399 °F
Molding
Mold Temperature 16.0 - 60.0 °C
60.8 - 140 °F
Drying Temperature 82.0 - 93.0 °C
180 - 199 °F
air dew point <-40°C