Bhansali Engineering Abstron HI-40 B ABS High Impact Injection Molding

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Bhansali Engineering
Trade Name Abstron
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Bhansali Engineering Abstron HI-40 B ABS High Impact Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Very High & Medium Impact, Paintable Automotive Grades Information provided by Bhansali
Physical Properties Metric English Comments
Density 1.045 g/cc
0.03775 lb/in³
ASTM D-792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D-955
Melt Flow 18 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 18 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D-1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 109
109
ASTM D-785
Tensile Strength, Yield 40.2 MPa

@Thickness 3.20 mm
 5830 psi

@Thickness 0.126 in
 Type 1; 5mm/min speed; ASTM D638
Flexural Yield Strength 57.9 MPa

@Thickness 6.40 mm
 8390 psi

@Thickness 0.252 in
 ASTM D790
Flexural Modulus 2.16 GPa

@Thickness 6.40 mm
 313 ksi

@Thickness 0.252 in
 ASTM D790
Izod Impact, Notched 3.7255 J/cm

@Thickness 6.40 mm
 6.9794 ft-lb/in

@Thickness 0.252 in
 ASTM D256
4.7059 J/cm

@Thickness 3.20 mm
 8.8161 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 94.0 °C
201 °F
Method A - Annealed; ASTM D-648
Vicat Softening Point 104 °C
219 °F
Method B; ASTM D-1525
Flammability, UL94 HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
 UL-94