Beijing Chemical Industry KAIFA® HN301-G0 PA6 Resin
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant |
| Manufacturer | Beijing Chemical Industry Research Institute (Group) |
| Trade Name | KAIFA® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Beijing Chemical Industry KAIFA® HN301-G0 PA6 Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flame retardant, Good flowInformation provided by Beijing Chemical Industry Research Institute (Group)
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 64.0 MPa | 9280 psi | ASTM D638 |
| Flexural Strength | 101 MPa | 14600 psi | ASTM D790 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.20 mm |
0.937 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Charpy Impact Unnotched | 5.10 J/cm² | 24.3 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.740 J/cm² | 3.52 ft-lb/in² | ISO179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 68.0 °C | 154 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 21.0 kV/mm @Thickness 2.00 mm |
533 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.028 @Frequency 1e+6 Hz |
0.028 @Frequency 1e+6 Hz |
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 210 °C | 392 - 410 °F | |
| Middle Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Front Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Nozzle Temperature | 235 - 240 °C | 455 - 464 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 60.0 - 90.0 MPa | 8700 - 13100 psi |
Users viewing this material also viewed the following:
- Polymax® Maxelast® C4860 TPE, Transparent
- Niche Polymer PA6GF13N Nylon 6, 13% Glass Fiber Filled
- PolyOne Geon™ Vinyl Wire & Cable WJKC302LR Polyvinyl Chloride, Flexible (PVC, Flexible)
- ICO Polymers ICOTEXâ„¢ 520-5005 1000 Micron EVA Powder
- MarkeTech Silicon Single Crystal Semiconductor Wafer, n-type, Phosphorous Doped, Float Zone Grown
- Fujipoly Industries Sarcon® 85Q Thin-Film QR
- Sylvin Technologies 9600-75 Clear PVC Molding Compound
- SABIC Innovative Plastics NORYL GTX GTX674PC PPE+PA6 (Europe-Africa-Middle East)
- EMS-Grivory Grivory® GVN-5H black 9915 PA*-GF50
- Blue River Coatings High Performance Acrylic Sanding Sealer
Copyright © lookpolymers.com All Rights Reserved