BASF Ultrason® E 2010 SW Q31 10088 PESU
| Category | Polymer , Thermoplastic , Polyethersulfone (PES) |
| Manufacturer | BASF |
| Trade Name | Ultrason® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultrason® E 2010 SW Q31 10088 PESU.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.700 - 0.800 g/cc | 0.0253 - 0.0289 lb/in³ | |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 2.2 % | 2.2 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.80 % | 0.80 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 56 | 56 | [cm<sup>3</sup>/g]; ISO 307 |
| Linear Mold Shrinkage, Flow | 0.0082 cm/cm | 0.0082 in/in | ISO 2577, 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0086 cm/cm | 0.0086 in/in | ISO 2577, 294-4 |
| Melt Flow | 95.9 g/10 min @Load 10.0 kg, Temperature 360 °C |
95.9 g/10 min @Load 22.0 lb, Temperature 680 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 154 MPa @Load 36.5 kg, Time 30.0 sec |
22300 psi @Load 80.5 lb, Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50mm/min; ISO 527-1/-2 |
| Elongation at Yield | 6.7 % | 6.7 % | 50mm/min; ISO 527-1/-2 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
28.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 75-1/-2 |
| 59.0 µm/m-°C @Temperature 180 °C |
32.8 µin/in-°F @Temperature 356 °F |
DIN 53752 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | ISO 11357-1/-2 |
| Decomposition Temperature | >= 400 °C | >= 752 °F | |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper throat |
| Zone 1 | 340 °C | 644 °F | Feed zone |
| Zone 2 | 350 °C | 662 °F | Compression |
| Zone 3 | 360 °C | 680 °F | Metering-zone |
| Zone 4 | 360 °C | 680 °F | Nozzle |
| Melt Temperature | 360 °C | 680 °F | Optimal |
| 340 - 390 °C | 644 - 734 °F | Injection molding/extrusion | |
| Mold Temperature | 140 - 180 °C | 284 - 356 °F | Injection molding |
| 160 °C | 320 °F | Optimal | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | 580-600°C | DIN 54836 |
| Primary Processing Technique | Injection molding |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8160 (UF) Synthetic Oil
- BASF Capron® SEG3 H1 15% Glass-Filled Nylon 6 (Dry) (discontinued **)
- BASF Master Builders Solutions ChemRex® CX-26 Isocyanate-Free Polyurethane-Based Sealant (discontinued **)<
- MarkeTech Zinc Oxide (ZnO) Single Crystal Substrate
- Solvay Specialty Polymers Galden® HT80 PFPE Heat Transfer Fluid
- Solvay Specialty Polymers Halar® 901 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE)
- Covestro Bayfill® EA 2003 Polyurethane Energy-Absorbing Semi-Rigid Foam, Friable Grade, MDI-based 2-Component Liquid System
- ConocoPhillips Hydroclear® 50 Power-D E.O. 50
- Polyplastics Duracon® M140-44/M140S Acetal Co-polymer (POM), Standard, High flow
- Chevron Phillips Marlex® HHM 5502LW Polyethylene; HDPE
Copyright © lookpolymers.com All Rights Reserved