Sharadaa Ceramics REFCAST ULCC90 Low Cement Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics REFCAST ULCC90 Low Cement Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: We bring to our clients a range of Low Cement Castables, that are available in varied alumina content and service range. Designed for abrasion resistance application, these are widely used in furnaces such as ladle back up lining, sintering furnace roof and soaking pit covers.Information provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | >= 3.00 g/cc | >= 0.108 lb/in³ | Dried at 110°C |
| Grain Size | <= 6000 µm | <= 6000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0118 GPa @Temperature 110 °C |
1.71 ksi @Temperature 230 °F |
|
| 0.0196 GPa @Temperature 1100 °C |
2.84 ksi @Temperature 2010 °F |
||
| 0.0255 GPa @Temperature 1500 °C |
3.70 ksi @Temperature 2730 °F |
||
| Compressive Strength | 68.6 MPa @Temperature 110 °C |
9960 psi @Temperature 230 °F |
Cold Crushing |
| 108 MPa @Temperature 1100 °C |
15600 psi @Temperature 2010 °F |
Cold Crushing | |
| 118 MPa @Temperature 1500 °C |
17100 psi @Temperature 2730 °F |
Cold Crushing | |
| 19.6 MPa @Time 86400 sec |
2840 psi @Time 24.0 hour |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 2.03 W/m-K @Temperature 400 °C, Time 10800 sec |
14.1 BTU-in/hr-ft²-°F @Temperature 752 °F, Time 3.00 hour |
|
| 2.09 W/m-K @Temperature 600 °C, Time 10800 sec |
14.5 BTU-in/hr-ft²-°F @Temperature 1110 °F, Time 3.00 hour |
||
| 2.15 W/m-K @Temperature 800 °C, Time 10800 sec |
14.9 BTU-in/hr-ft²-°F @Temperature 1470 °F, Time 3.00 hour |
||
| Maximum Service Temperature, Air | 1750 °C | 3180 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | >= 90 % | >= 90 % | |
| Fe2O3 | <= 0.60 % | <= 0.60 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | -0.2 - 0.2% | 800°C |
| -0.3 - 0.3% | 1100°C | |
| -0.8 - 0.8% | 1500°C | |
| Refractoriness | >1820°C | |
| Thermal Expansion | 0.9 | 1000°C, Reversible |
| Water Required to Mix | 4.5 - 5% |
Users viewing this material also viewed the following:
- Polykemi AB POLYform POM C M90 S10 Polyoxymethylene, Impact Modified
- Magyar Aluminum ALO-DFC Alumina
- IDI Composites M-205 Thermoset Polyester, Sheet
- Techmer ES Plastiblend® TPX-HTN-000AB 15% Glass Filled
- A. Schulman PP 3466-01 Polypropylene Homopolymer Polypropylene
- Entec Hylac® EX18 ABS
- DuPont Teijin Films Melinex® 329 Polyester Film, 300 Gauge
- Eurotec® Tecotek® PC30 NL TD 700 PC, unfilled, flame retardant - halogen (RoHS compliant), impact modified, natural
- Ametek High Purity Nickel Strip 899A 1/2 Hard
- ATI Allegheny Ludlum AL 625HP™ Stainless Steel
Copyright © lookpolymers.com All Rights Reserved